Polypropylene Copolymer
Borealis AG
產品說明：
BB125MO is a heterophasic copolymer. This grade is a low melt flow rate grade intended for blow moulding and sheet extrusion, and features extremely good processability with improved melt strength and melt stability. As all polypropylenes, this grade shows excellent stress-cracking and chemical resistances.
This polymer is one of the IMP (improved mechanical stability) grades, and is characterized by very high stiffness without any loss of impact strength even at low temperatures.
物性信息：
| 特性 | 剛性，高 高 ESCR（抗應力開裂） 共聚物 較高的熔體穩定性 抗撞擊性，良好 可加工性，良好 良好的熔體強度 流動性低 耐低溫沖擊 耐化學性良好 |
| 用途 | 波形板 工業容器 工業應用 |
| 形式 | 粒子 |
| 加工方法 | 吹塑成型 片材擠出成型 |
| 密度 | 0.905 | g/cm3 | ISO 1183 |
| 熔流率（熔體流動速率） | ISO 1133 | ||
| 190°C/5.0 kg | 2.3 | g/10 min | ISO 1133 |
| 230°C/2.16 kg | 1.3 | g/10 min | ISO 1133 |
| 230°C/5.0 kg | 6.0 | g/10 min | ISO 1133 |
| 拉伸模量 | 1300 | MPa | ISO 527-2/50 |
| 拉伸應力 (屈服) | 25.0 | MPa | ISO 527-2/50 |
| 拉伸應變 (屈服) | 5.0 | % | ISO 527-2/50 |
| 彎曲模量 | 1200 | MPa | ISO 178 |
| 簡支梁缺口沖擊強度 | ISO 179/1eA | ||
| -20°C | 7.0 | kJ/m2 | ISO 179/1eA |
| 23°C | 50 | kJ/m2 | ISO 179/1eA |
| 熱變形溫度 (0.45 MPa, 未退火) | 85.0 | °C | ISO 75-2/B |
| 料筒1區溫度 | 190 到 220 | °C | |
| 料筒2區溫度 | 190 到 220 | °C | |
| 料筒3區溫度 | 190 到 220 | °C | |
| 料筒4區溫度 | 190 到 220 | °C | |
| 料筒5區溫度 | 190 到 220 | °C | |
| 熔體溫度 | 180 到 220 | °C | |
| 口模溫度 | 180 到 220 | °C |