Jupiter-AAA鑄鐵焊條
Shield Metal Arc Welding(SMAW - Stick)
手工焊條電弧焊（SMAW-Stick）
For all cast irons - Meehanite, ductile, mealleable, gray cast irons and steel to cast iron.
適用于所有鑄鐵-Meehanite孕育鑄鐵、球墨鑄鐵、可鍛鑄鐵、灰口鑄鐵，以及鋼至鑄鐵的焊接。
Features
亮點
High Strength Up To 70,000psi/482MPa
抗拉強度高達70,000psi/482MPa
No Electrode Overheating
無焊條過熱
Smooth Ductile Deposits
平滑韌性熔敷層
Steel To Cast Iron
鋼和鑄鐵的焊接
More Efficient Deposits
更高效的熔敷
All Weldable Grades Of Cast Iron
所有可焊接等級的鑄鐵
Machinable Deposit
可加工熔敷層
Eliminates Porosity
無氣孔
Characteristics
Jupiter AAA is engineered to give the user a high strength ductile weld without electrode overheating, thus producing a much more efficient deposit that is machinable. Welds are typically smooth, porosity free and flat. Excellent tie in between passes.
Jupiter AAA的設計目的是為用戶提供高強度的韌性焊縫，而不會使焊條過熱，從而更高效的產生可加工的熔敷層。焊縫通常光滑、無氣孔且平整。出色的焊道間結合。
Jupiter AAA makes it easier and more cost effective to do large cast iron repairs. It can be used on dirty and oil impregnated pieces without the problem of electrode overheating. Superior choice for joining cast iron to steel.
Jupiter AAA使大型鑄鐵維修變得更容易、更具成本效益。它可以用于臟的和含油浸的工件，而不會出現焊條過熱的問題。鑄鐵與鋼連接的理想選擇。
Technical技術參數
Size and Amps AC/DC+(DCEP)
|
Inches |
3/32 |
1/8 |
5/32 |
3/16 |
|
(mm) |
(2.4) |
(3.2) |
4.0 |
5.0 |
|
Amps |
65-90 |
70-130 |
100-175 |
200-275 |
Best Practices Application 應用
Remove cracks using grinder or Electra.
去除裂縫.
Stop drill cracks ends.
止裂孔。
Use medium arc and stringer beads.
使用中等弧長和線狀焊道。
Skip weld, light peening recommended.
跳焊，建議輕敲擊。
For critical or heavy parts preheat to 500?F(260?C).
對于關鍵或重型零件，預熱至500?F(260?C)。
Cool slowly after welding. 焊后緩冷。